Preparation and Thermoluminescence Properties of Polycrystalline Na2SO4/SiO2 composite
DOI:
https://doi.org/10.15392/2319-0612.2024.2322Palavras-chave:
TLD, Geode, SilicaResumo
A sodium sulphate/silica (Na2SO4/SiO2) composite was prepared by a sol-gel procedure using a geode as the silica source. The prepared sample was characterized by XRD, XRF and IR techniques. The Na2SO4/SiO2 has an orthorhombic phase, and an average crystalline size is about 51 nm. Thermoluminescence characteristics of Na2SO4/SiO2 were studied at different parameters. The glow curve resulting from Na2SO4/SiO2 showed one clear peak between 150 oC to 200 oC, depending on the energy. The general peak structure of the TL glow curve remains unchanged as a result of repeated cycles of irradiation at various X–ray energies, and exhibits good linearity over the used exposure. There were no significant changes in the TL reading after ten times of reuse, and the fading was observed at 56% after 15 days of irradiation and after one month about 82.3% of the TL signal was lost, and the value of Zeff of Na2SO4/SiO2 was found to be 13.56.
Downloads
Referências
KRON, T. Thermoluminescence dosimetry and its applications in medicine-Part 1: Physics, materials and equipment. Australasian Physical and Engineering Sciences in Medicine. 1994, 17, 175–199.
MOSCOVITCH, M.; JOHN, T.J.; CASSATA, J. R.; BLAKE, P. K.; ROTUNDA, J. E.; RAMLO, M.; VELBECK, K.J.; LUO, L. Z. The application of LiF:Mg,Cu,P to large scale personnel dosimetry: Current status and future directions. Radiation Protection Dosimetry. 2006, 119, 248–254.
CHAND, S.; MEHRA, R.; CHOPRA, V. Recent developments in phosphate materials for their thermoluminescence dosimeter (TLD) applications. Luminescence 2021, 36, 1808–1817.
Preusser, F.; Chithambo, M. L.; Götte, T.; Martini, M.; Ramseyer, K.; Sendezera, E. J.; Susino, G. J.; Wintle, A.G. Quartz as a natural luminescence dosimeter. Earth Science Reviews. 2009, 97, 184–214.
Thamóné Bozsó, E.; Füri, J.; Kovács István, J.; Biró, T.; Király, E.; Nagy, A.; Törökné Sinka, M.; Kónya, P.; Mészárosné Turi, J.; Vígh, C. Characteristics of quartz separates of different formations in Hungary from the aspect of osl dating. Foldt. Kozlony 2020, 150, 61.
Bailiff, I. K.; Stepanenko, V. F.; Göksu, H.Y.; Bøtter-Jensen, L.; Brodski, L.; Chumak, V.; Correcher, V.; Delgado, A.; Golikov, V.; Jungner, H.; et al. Comparison of retrospective luminescence dosimetry with computational modeling in two highly contaminated settlements downwind of the chernobyl NPP. Health Physics. 2004, 86, 25–41.
BENEITEZ, P.; CORRECHER, V.; MILLAN, A.; CALDERON, T. Thermoluminescence analysis for testing the irradiation of spices. Journal of Radioanalytical and Nuclear Chemistry. 1994, 185, 401–410.
ELDER. J. P., Thermal energy storage materials-a DSC study, Thermochimica Acta, vol. 36, no. 1, 1980. pp. 67–77.
WIEDEMANN. H. G., Thermal studies on thenardite, Thermochimica Acta, vol. 50, no. 1–3, 1981. pp. 17–29.
VIDYA .Y. S.; LAKSHMINARASAPPA .B. N. Preparation, Characterization, and Luminescence Properties of Orthorhombic Sodium Sulphate, Physics Research International Volume 2013, Article ID 641631, 7 pages.
WANG, W. L. ; YANG, X. X. ; FANG, Y.T. ; DING, J., Preparation and performance of form-stable polyethylene glycol/silicon dioxide composites as solid-liquid phase change materials, Applied Energy., 86, 2009.170 -174
ARUN KUMAR D. ; MERLINE SHYLA J. ; FRANCIS P. XAVIER. Synthesis and characterization of TiO2/SiO2 nano composites for solar cell applications, Applied Nanoscience 2, 2012. pp. 429-436.
ZHANG Y. JIN S. ; YANG Y. ; CHUNSHENG Y. Annealing effects on the phase and microstructure transformations of nanocrystalline (ZrO2)1−x(Sc2O3)x (x=0.02-0.16) thin films deposited by sol-gel method. Solid State Communications. 2002 .122 7-8, 439 444.
RAVIKUMAR, N. R.; ARUN KUMAR, B. S.; PANIGRAHI, U. ; DHUSOODANAN, C. B. ; PALAN, AND S. K. OMANWAR. Spectral and Thermoluminescence Characteristics of High Gamma Dose Irradiated Dy:LiKB4O7 Single Crystals. Nuclear Instruments and Methods in Physics Research, Section B: Beam Interactions with Materials and Atoms 436(September) 2018 :203–10.
CHEN, R.; PAGONIS, V.; LAWLESS, J. L. Evaluated thermoluminescence trapping parameters-What do they really mean? Radiation Measurements. 2016, 91, 21–27.
MAGHARBI. M. ; ARAFAH D. E. ; Sensitization of the thermoluminescence response of CaF2 phosphors, Physica Status Solidi (A), vol. 195, no. 2, 2003. pp. 459–467.
HAMZAH, S. A.; SAEED M. A.; WAGIRAN. H.; AND HASHIM. I. H.; Thermoluminescence (TL) Dosimeter of Dysprosium Doped Strontium Borate Glass for Different Glass Modifiers (Na, Li, Ca) Subjected from 1 to 9 Gy Doses. EPJ Web of Conferences 2017.156:1–6.
MOHAMMED BAHRA,; JAAFAR. M. S.; AND WAGIRAN. H.; Thermoluminescence Dosimetry Properties and Kinetic Parameters of Zinc Borate Silica Glass Doped with Cu2O and Co-Doped with SnO2. Journal of Luminescence 204 (December 2017):375–81
FURETTA, C.; Handbook of thermoluminescence: 2nd ed. Singapore: World Scientific, 2010.
Downloads
Publicado
Edição
Seção
Licença
Direitos autorais (c) 2024 Brazilian Journal of Radiation Sciences
Este trabalho está licenciado sob uma licença Creative Commons Attribution 4.0 International License.
Declaro que o presente artigo é original, não tendo sido submetido à publicação em qualquer outro periódico nacional ou internacional, quer seja em parte ou em sua totalidade. Declaro, ainda, que uma vez publicado na revista Brazilian Journal of Radiation Sciences, editada pela Sociedade Brasileira de Proteção Radiológica, o mesmo jamais será submetido por mim ou por qualquer um dos demais co-autores a qualquer outro periódico. Através deste instrumento, em meu nome e em nome dos demais co-autores, porventura existentes, cedo os direitos autorais do referido artigo à Sociedade Brasileira de Proteção Radiológica, que está autorizada a publicá-lo em meio impresso, digital, ou outro existente, sem retribuição financeira para os autores.
Licença
Os artigos do BJRS são licenciados sob uma Creative Commons Atribuição 4.0 Licença Internacional, que permite o uso, compartilhamento, adaptação, distribuição e reprodução em qualquer meio ou formato, desde que você dê o devido crédito ao (s) autor (es) original (is) e à fonte, forneça um link para a licença Creative Commons, e indique se mudanças foram feitas. As imagens ou outro material de terceiros neste artigo estão incluídos na licença Creative Commons do artigo, a menos que indicado de outra forma em uma linha de crédito para o material. Se o material não estiver incluído no licença Creative Commons do artigo e seu uso pretendido não é permitido por regulamentação legal ou excede o uso permitido, você precisará obter permissão diretamente do detentor dos direitos autorais. Para visualizar uma cópia desta licença, visite http://creativecommons.org/licenses/by/4.0/