The recycling through melting Zircaloy machining chips, preliminary results
DOI:
https://doi.org/10.15392/bjrs.v6i2.425Palavras-chave:
Zircaloy, nuclear fuel, recycling, cladding, electron beam meltingResumo
PWR (Pressurized Water Reactor) reactors employ as nuclear fuel UO2 pellets packed in zirconium alloy tubes, called cladding. In the manufacture of the tubes, machining chips are generated which can not be discarded, since the recycling of this material is strategic in terms of nuclear technology, legislation, economics and the environment. These nuclear alloys are very expensive and are not produced in Brazil and are imported for the manufacture of nuclear fuel. In this work, we will discuss methods not yet studied to recycle Zircaloy chips using electron beam furnaces in order to obtain ingots. In addition, it is intended to carry out the melting of new Zircaloy alloys, from the fusion of zirconium sponge produced in IPEN and imported and Zircaloy bars. The mechanical properties and the present phases of the material should be determined, as well as, the characterization of the microstructures by optical microscopy. This work, therefore, aims at the creation of a new line of research where methods will be approached to recycle the chips and to reduce in 30 times by means of fusion the enormous volume of material stored in the form of machining chips, being able to do others components for nuclear or chemical industry use, as well as conducting basic development research.
Downloads
Referências
MUKHERJEE, P.; SARKAR, A.; BARAT, P.; BANDYOPADHYAY, S.K. et al. Micro-structural studies on lattice imperfections in deformed zirconium-base alloys by X-ray diffraction. Metallurgical Materials Trans. v. 31A, p. 2405–9, 2000.
STEINBRÜCK, M. Hydrogen absorption by zirconium alloys at high temperatures. Journal of Nuclear Materials, v. 334(1), p. 58–64, 2004. Available from: http://linkinghub.elsevier.com/retrieve/pii/S0022311504004799
Standard specification for hot-rolled and cold-finished zirconium and zirconium alloy bars, rod, and wire for nuclear application. ASTM: B351-08. ASTM-American Soc. Testing Materials.
YILMAZBAYHAN, A.; MOTTA, A.T.; COMSTOCK, R.J. et al. Structure of zirconium alloy oxides formed in pure water studied with synchrotron radiation and optical microscopy: rela-tion to corrosion rate. Journal of Nuclear Materials, v. 324(1), p.6–22, 2004.
DAYTON, R.W.; ALLEN, C.M.; EBERTS, W.U. The reclamation of zirconium machining chips to produce arc-melting feed stock. United States at Energy Comm.; AECD-3499, 1952.
MIMURA, K.; LEE, S-W.; ISSHIKI, M. Removal of alloying elements from zirconium al-loys by hydrogen plasma-arc melting. Journal of Alloys Compounds, v. 221(1–2), p. 267–73, 1995. Available from: http://linkinghub.elsevier.com/retrieve/pii/0925838894014701.
BOHE, A.E.; ANDRADE GAMBOA, J.J.; LOPASSO, E.M.; PASQUEVICH, D.M. Zir-conium recovery from Zircaloy shavings. Journal of Material Science, v. 31, p. 3469–74, 1996.
PEREIRA, L.A.T. Desenvolvimento de processos de reciclagem de cavacos de zircaloy via refusão em forno elétrico a arco e metalurgia do pó. Nuclear and Energy Research Institute - IP-EN. Tese., 2014.
MENG, X.; NORTHWOOD, D. Second phase particles in Zircaloy-2. Journal of Nuclear Materials; v. 168, p. 125–36, 1989.
VIZCAINO, P.; BANCHIK, A.D.; ABRIATA, J.P. Synchrotron X-ray diffraction evidenc-es of the amorphization/dissolution of the second phase particles (SPPs) in neutron irradiated Zircal-oy-4. Material Letter, v. 62(3), p. 491–3, 2008.
Standard Test Methods for Tension Testing of Metallic Materials - ASTM E8/E8M. ASTM-American Soc. Testing Materials. p. 1–27, 2009.
VANDER VOORT, G.F. Metallography - Principles and Practice. ASM International, 1999.
DANIELSON, P.E. and SUTHERLIN, R.C. Metallography and microstructures of zirconi-um, hafnium, and their alloys. In: Metallography and Microstructures, ASM Handbook, v. 9, p. 942–958, 2004.
Downloads
Publicado
Edição
Seção
Licença
Declaro que o presente artigo é original, não tendo sido submetido à publicação em qualquer outro periódico nacional ou internacional, quer seja em parte ou em sua totalidade. Declaro, ainda, que uma vez publicado na revista Brazilian Journal of Radiation Sciences, editada pela Sociedade Brasileira de Proteção Radiológica, o mesmo jamais será submetido por mim ou por qualquer um dos demais co-autores a qualquer outro periódico. Através deste instrumento, em meu nome e em nome dos demais co-autores, porventura existentes, cedo os direitos autorais do referido artigo à Sociedade Brasileira de Proteção Radiológica, que está autorizada a publicá-lo em meio impresso, digital, ou outro existente, sem retribuição financeira para os autores.
Licença
Os artigos do BJRS são licenciados sob uma Creative Commons Atribuição 4.0 Licença Internacional, que permite o uso, compartilhamento, adaptação, distribuição e reprodução em qualquer meio ou formato, desde que você dê o devido crédito ao (s) autor (es) original (is) e à fonte, forneça um link para a licença Creative Commons, e indique se mudanças foram feitas. As imagens ou outro material de terceiros neste artigo estão incluídos na licença Creative Commons do artigo, a menos que indicado de outra forma em uma linha de crédito para o material. Se o material não estiver incluído no licença Creative Commons do artigo e seu uso pretendido não é permitido por regulamentação legal ou excede o uso permitido, você precisará obter permissão diretamente do detentor dos direitos autorais. Para visualizar uma cópia desta licença, visite http://creativecommons.org/licenses/by/4.0/